%0 journal article %@ 0921-5093 %A Winzer, N., Atrens, A., Dietzel, W., Song, G., Kainer, K.U. %D 2008 %J Materials Science and Engineering A %N 1-2 %P 97-106 %R doi:10.1016/j.msea.2007.03.021 %T Comparison of the Linearly Increasing Stress Test and the Constant Extension Rate Test in the Evaluation of Transgranular Stress Corrosion Cracking of Magnesium %U https://doi.org/10.1016/j.msea.2007.03.021 1-2 %X measuring the threshold stress and crack velocity. During a LIST fast fracture ensues a relatively short time after the threshold stress is attained, whereas during CERT crack growth over a much longer time period is facilitated by a reduction in stress. Consequently, the LIST is typically 30 - 50 % shorter in duration, whereas the CERT produces a larger SCC fracture surface.