@misc{daconceicao_on_the_2010, 
author={da Conceicao, T.F., Scharnagl, N., Dietzel, W., Kainer, K.U.},
title={On the degradation mechanism of corrosion protective poly(ether imide) coatings on magnesium AZ31 alloy},
year={2010},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.corsci.2010.06.008},
abstract = {In previous publications of the authors, good performance of poly(ether imide) as corrosion protective coatings for magnesium AZ31 alloy was reported. It was suggested that during the sample degradation magnesium hydroxide could react with the imide ring forming magnesium polyamate and polyamic acid, but this could not be experimentally confirmed. In the present letter, we confirm the occurrence of this reaction by infrared and X-ray photoelectron spectroscopy and discuss its influence in the corrosion behavior observed in electrochemical impedance spectroscopy tests.},
note = {Online available at: \url{https://doi.org/10.1016/j.corsci.2010.06.008} (DOI). da Conceicao, T.; Scharnagl, N.; Dietzel, W.; Kainer, K.: On the degradation mechanism of corrosion protective poly(ether imide) coatings on magnesium AZ31 alloy. Corrosion Science. 2010. vol. 52, no. 10, 3155-3157. DOI: 10.1016/j.corsci.2010.06.008}}